The surfaces of polypropylene (PP) and polystyrene (PS) thin films were subjected to oxygen plasma treatment, produced by glow discharge (direct current, vacuum chamber, temp. 27-30°C, pressure 200Pa). The effects of time (up to 110s) and power (1W or 5W) of the treatment on the values of free energy (γs) of PS and PP samples and γs components - dispersive (γsD) and polar (γsP) ones - were determined. With prolonged time of interaction the values of γs and γsP increased, especially in the region of first 35-50s, while γsD values kept the similar level during the whole time of exposure. The dependence of PP and PS surface resistance on the same parameters as above (time and power of interaction) has been also found. For both polymers this resistance decrease with prolonged time and growing power of exposure.
Powierzchnie cienkich folii polipropylenowych (PP) i polistyrenowych (PS) poddawano działaniu plazmy tlenowej uzyskiwanej pod wpływem wyładowań jarzeniowych (prąd stały, komora próżniowa, temp. 27-30°C, ciśnienie 200Pa). Określono wpływ czasu (do 110s), a także mocy (1W lub 5W) takiego oddziaływania na wartość swobodnej energii powierzchniowej (γs) próbek PP i PS oraz składowych γs - dyspersyjnej (γsD) i polarnej (γsP) (rys. 1-4). Z przedłużaniem czasu oddziaływania wartości γs i γsP zwiększały się, zwłaszcza wyraźnie w przedziale pierwszych 35-50s, natomiast wartości γsD utrzymywały się na zbliżonym poziomie w ciągu całego okresu ekspozycji. Określono także zależność oporności powierzchniowej PP i PS od tych samych parametrów (czasu oraz mocy oddziaływania - rys. 5 i 6). W przypadku obydwu typów polimerów oporność ta maleje wraz z przedłużaniem czasu i zwiększeniem mocy ekspozycji.