The results of research into the microstructure and mechanical properties of Fe73T5Y3B19, Fe61Co10Y8Ti1B20 alloys are presented in this paper. Samples were obtained at the solidification speed of 104÷106 K/s in the form of ribbons of about 30 µm in thickness. All studies were conducted for samples in the as-cast state. Amorphous structure of the investigated alloys was confirmed by the X-ray diffractometry. The chemical composition determined from EDS studies was similar to the nominal composition of the alloy. Photos of the Vickers imprints, and the abrasion areas were obtained using an optical microscope for the matte side of the tape. The obtained results showed that the alloy with higher titanium content had much higher abrasion resistance as well as greater surface development.
W pracy przedstawiono wyniki badań mikrostruktury oraz wybranych właściwości mechanicznych stopów Fe73T5Y3B19, Fe61Co10Y8Ti1B20 otrzymanych przy prędkości krzepnięcia 104÷106 K/s w postaci cienkich taśm o grubości około 30 µm. Badania przeprowadzono dla próbek stopów w stanie po zestaleniu. Amorficzność stopów potwierdzono badaniami rentgenowskimi. Skład chemiczny próbek został wyznaczony na podstawie badań z wykorzystaniem spektrometru rentgenowskiego EDS i jest zbliżony do nominalnego składu stopu. Zdjęcia próbek, odcisków Vickersa oraz obszarów wytarć wykonano z wykorzystaniem mikroskopu świetlnego. W pracy przedstawiono wyniki badań dla matowej strony taśmy. Wyniki badań zamieszczone w tej pracy pokazują, że stop z większą zawartością tytanu cechuje się znacznie większą odpornością na ścieranie, jak również większym rozwinięciem powierzchni.