The work presents the study of coatings made in the process of magnetron sputtering of AISI310S grade chromium-nickel steel. The study covered coatings of the steel’s composition with an additions of 2–5% Si and of 2–5% Al. The coatings provided a resistance element in the electric circuit, and the measurement of their temperature was made by the voltage drop indirect method. It was found that the steel coatings had a resistance of 0.176 Ω within the entire range of testing temperature, and their failure occurred at a temperature of 350oC due to cracking and delamination from the substrate. Introducing the Si or Al addition to the coatings resulted in an increase in coating resistance and temperature stability, to 450 and 400oC, respectively. It was found that the durability evaluation method to influence coatings performance characteristics.
W pracy przedstawiono badania powłok PVD wykonanych w procesie magnetronowego rozpylania stali chromowo-niklowej gatunku X8CrNi25-21. Badano powłoki o składzie stali z domieszkami krzemu 2–5% i aluminium 2–5%. Badano trwałość powłok w temperaturach indukowanych przepływem prądu elektrycznego. Wykazano, że powłoki osadzone na monokrystalicznym krzemie posiadają rezystancję 0,176 Ω, a ich uszkodzenie następuje w temperaturze 3500C. Wprowadzenie do powłok domieszek krzemu lub aluminium powoduje wzrost ich oporności oraz trwałości temperaturowej odpowiednio do 450 i 400oC. Stwierdzono, że metoda oceny trwałości powłok ma wpływ na właściwości eksploatacyjne.