The supermolecular structure of pine wood after mercerisation by sodium hydroxide was investigated by means of wide-angle x-ray scattering (WAXS). The relationship between the condition of mercerised pine wood (Pinus silvestris L.) and the degree of transformation from cellulose I to cellulose II were analysed. It was found that the amount of cellulose II depends on the concentration of NaOH solution as well as on the time of chemical activation. The greatest efficiency of polymorphic transition of cellulose was noted in the highest concentration of sodium hydroxide solution (20 and 25%). Moreover, the rate of polymorphic conversion of cellulose by the decrease in the crystallinity of wood was estimated.
W pracy badano strukturę nadcząsteczkową drewna sosnowego poddanego procesowi merceryzacji wodorotlenkiem sodu za pomocą szerokokątowej dyfrakcji promieni rentgenowskich (WAXS). Przeprowadzono analizę wpływu stosowanych warunków procesu merceryzacji na stopień transformacji fazowej celulozy I do celulozy II. Stwierdzono, że ilość celulozy II, indukowanej w procesie alkalizacji, silnie zależy od stężenia roztworu wodorotlenku sodu oraz od czasu chemicznej aktywacji drewna sosnowego. Największą efektywność transformacji fazowej w celulozie zanotowano przy stosowaniu najwyższych stężeń roztworów NaOH, tj. 20 % i 25 %. Ponadto, proces merceryzacji drewna sosnowego spowodował spadek stopnia krystaliczności celulozy.