In this paper the reliability assessment of structural reliability of the selected light-cured dental composites based on the biaxial flexural strength test results has been presented. A two-parameter Weibull distribution was applied as a reliability model in order to estimate probability of strength maintenance in the analysed population. Weibull distribution parameters were interpreted as a characteristic material strength (scale parameter) and structural reliability parameter in terms of ability to maintain strength by each of specimen from the general population (shape parameter). 20 composite specimens underwent strength tests, including 2 "flow" type composites and 2 standard composites (with typical filler content). "Flow" type composites were characterized with lower characteristic strength and higher structural reliability comparing to other studied composites.
W artykule przedstawiono ocenę niezawodności strukturalnej wybranych światłoutwardzalnych kompozytów stomatologicznych na podstawie wyników testu wytrzymałości na zginanie dwuosiowe. Wykorzystano dwuparametrowy rozkład Weibull’a jako model niezawodności w celu oszacowania prawdopodobieństwa zachowania wytrzymałości materiału w analizowanej populacji. Parametry rozkładu Weibull’a interpretowano jako wytrzymałość charakterystyczną materiału (parametr skali) oraz wskaźnik niezawodności strukturalnej w sensie zdolności do zachowania charakterystycznej wytrzymałości przez każdy z egzemplarzy populacji generalnej (parametr kształtu). Próbie wytrzymałościowej poddano po 20 próbek kompozytów, w tym 2 kompozyty typu ,,flow” oraz 2 kompozyty standardowe (z typową ilością wypełniacza). Kompozyty typu ,,flow” charakteryzowały się niższą wytrzymałością charakterystyczną oraz wyższą niezawodnością strukturalną w porównaniu z pozostałymi badanymi kompozytami.