This article is devoted to interlaminar cracking research on carbon multidirectional fibrous-epoxy composites. Composite beams with 0°/0° 0°/45° and 0°/90° interfaces were subjected to double cantilever beam tests whereby force-crack opening displacement curves were determined. Additionally, crack length observations were conducted in order to determine the crack resistance curves of multidirectional composites. On the basis of the performed tests, it was found that the critical strain energy release rate for crack initiation is size independent of the material configuration. On the other hand, the fiber orientation is crucial to the critical strain energy release rate for crack propagation.
Artykuł dotyczy badań odporności na pękanie wielokierunkowych kompozytów epoksydowo-włóknistych na bazie włókien węglowych. Belki kompozytowe z interfejsami 0°/0° 0°/45° oraz 0°/90° zostały zbadane za pomocą metody Double Cantilever Beam, w których wyznaczono charakterystyki siła - wielkość rozwarcia szczeliny. Dodatkowo prowadzono obserwacje długości pęknięcia w celu wyznaczenia krzywych odporności na pękanie kompozytów wielokierunkowych. Na podstawie przeprowadzonych badań stwierdzono, że wartość krytycznego współczynnika uwalniania energii dla inicjacji pęknięcia jest wielkością niezależną od ukierunkowania włókien. Natomiast ułożenie włókien jest kluczowe w przypadku krytycznego współczynnika uwalniana energii dla propagacji pęknięcia.