The Infona portal uses cookies, i.e. strings of text saved by a browser on the user's device. The portal can access those files and use them to remember the user's data, such as their chosen settings (screen view, interface language, etc.), or their login data. By using the Infona portal the user accepts automatic saving and using this information for portal operation purposes. More information on the subject can be found in the Privacy Policy and Terms of Service. By closing this window the user confirms that they have read the information on cookie usage, and they accept the privacy policy and the way cookies are used by the portal. You can change the cookie settings in your browser.
Corrosion products at the steel/concrete interface of specimens subjected to different environments were examined. The process of generation of the corrosion product-filled paste (CP), including the corrosion products filling in air voids, was observed. The tiny cracks caused by the artificially accelerated corrosion process were observed to favour CP growth. The thicknesses of CP and the corrosion...
Corrosion layers at the steel/concrete interfaces of two reinforced concrete specimens subjected to chloride ion ingress were observed and measured by SEM. A Gaussian function was used to model the distribution of the non-uniform corrosion. The physical meaning of the parameters in the Gaussian model is confirmed mathematically and the relationships among these parameters are discussed. The locations...
Set the date range to filter the displayed results. You can set a starting date, ending date or both. You can enter the dates manually or choose them from the calendar.