The Infona portal uses cookies, i.e. strings of text saved by a browser on the user's device. The portal can access those files and use them to remember the user's data, such as their chosen settings (screen view, interface language, etc.), or their login data. By using the Infona portal the user accepts automatic saving and using this information for portal operation purposes. More information on the subject can be found in the Privacy Policy and Terms of Service. By closing this window the user confirms that they have read the information on cookie usage, and they accept the privacy policy and the way cookies are used by the portal. You can change the cookie settings in your browser.
The oxidation behavior of the Co-base superalloy DZ40M was studied in air at900–1100°C for times of up to 2000 hr. The results indicated thatthis alloy can grow a protective oxide scale at 900 and 1000°C duringisothermal oxidation, but not at 1100°C because of serious cracking andspalling of the oxide scales. Moreover, an internal-precipitate zone formedin the subsurface region of the alloy at all...
A surface-morphology change has been observed for an aluminide coating on the Co-base superalloy DZ40M during oxidation at 1100°C in air. The oxide formed on the coating remained an even grayish-white color during the stable oxidation stage, whereas, dark-colored corrosion nodules were observed when oxidation of the coating accelerated. The number of nodules increased with time, along with growth...
Set the date range to filter the displayed results. You can set a starting date, ending date or both. You can enter the dates manually or choose them from the calendar.