The Infona portal uses cookies, i.e. strings of text saved by a browser on the user's device. The portal can access those files and use them to remember the user's data, such as their chosen settings (screen view, interface language, etc.), or their login data. By using the Infona portal the user accepts automatic saving and using this information for portal operation purposes. More information on the subject can be found in the Privacy Policy and Terms of Service. By closing this window the user confirms that they have read the information on cookie usage, and they accept the privacy policy and the way cookies are used by the portal. You can change the cookie settings in your browser.
Magnetostrictive Fe 83 Ga 17 wires 0.6mm in diameter were prepared successfully by directional solidification, heat swaging and drawing. The <100> crystallographic texture was developed after recrystallization annealing. A large Wiedemann twist up to 245′′/cm was observed in annealed wires. The large Wiedemann twist could be attributed to the large magnetostriction of 160ppm...
1.0at.% B-doped Fe 83 Ga 17 sheets 0.05mm thick were successfully prepared. A sheet with “cube texture” of {001}〈100〉 was obtained in the rolled sheets. The temperature and deformation rate in the rolling process and the final annealing atmosphere were all controlled precisely. A large magnetostrictive strain (λ‖) of up to 170ppm was achieved in the 0.26mm thick rolled sheets under...
Set the date range to filter the displayed results. You can set a starting date, ending date or both. You can enter the dates manually or choose them from the calendar.