The Infona portal uses cookies, i.e. strings of text saved by a browser on the user's device. The portal can access those files and use them to remember the user's data, such as their chosen settings (screen view, interface language, etc.), or their login data. By using the Infona portal the user accepts automatic saving and using this information for portal operation purposes. More information on the subject can be found in the Privacy Policy and Terms of Service. By closing this window the user confirms that they have read the information on cookie usage, and they accept the privacy policy and the way cookies are used by the portal. You can change the cookie settings in your browser.
The effect of thermal aging on the microstructure evolution and solder joint reliability in hard disk drive (HDD) under mechanical shock was investigated. Significant coarsening of Ag3 Sn particles was found in SnAgCu solder, and AuSn4 intermetallic compound (IMC) changed from needle-type to layer-type during aging. For as-soldered SnAgCu solder joints after mechanical shock, the cracks were initiated...
The interfacial microstructure evolution between Sn-3.5Ag-0.75Cu solder ball and Au/Ni/Cu pad was investigated under as-bonded and thermal aging conditions. Moreover, the shear and mechanical shock tests were carried out to study the failure mechanisms. Results showed that only one intermetallic compound, fine needle-like AuSn4 was found at the solder/pad interface under as-bonded condition. After...
Set the date range to filter the displayed results. You can set a starting date, ending date or both. You can enter the dates manually or choose them from the calendar.