The Infona portal uses cookies, i.e. strings of text saved by a browser on the user's device. The portal can access those files and use them to remember the user's data, such as their chosen settings (screen view, interface language, etc.), or their login data. By using the Infona portal the user accepts automatic saving and using this information for portal operation purposes. More information on the subject can be found in the Privacy Policy and Terms of Service. By closing this window the user confirms that they have read the information on cookie usage, and they accept the privacy policy and the way cookies are used by the portal. You can change the cookie settings in your browser.
In this paper, the microstructure, mechanical properties, and corrosion behavior of friction stir welded (FSW) joints of the two aluminum alloys 6005A‐5083 were investigated and their correlation was discussed. In contrast to FSW joints of the same aluminum material, this results in a “V” shape curve of hardness distributed nonsymmetrically along the weld. The lowest hardness area occurs at the interface...
The effects of the intergranular corrosion (IGC) defect depth on the high circle fatigue performance of tungsten inert gas (TIG)‐welded joints of 6005A–5083 dissimilar aluminum alloys were investigated. After soaking in different IGC solutions for 72 h, corrosion defects of different depths were generated in various areas of the specimen surfaces. It was found that the 5083 base metal exhibited the...