Using flax stem and ferrous sulfate, a composite porous carbon material was prepared by means of high‐temperature roasting and a one‐step process in a muffle furnace. The samples were characterized using X‐Ray diffraction (XRD) and Scanning electron microscopy (SEM), and the effects of ferrous sulfate concentration, carbonization temperature, and pH values of Cr(VI) aqueous solution on the removal performance of Cr(VI) were studied. XRD and SEM analysis showed that the prepared samples were amorphous porous carbon loaded with FeS/Fe2O3/Fe3O4. High FeSO4 impregnation concentration, high carbonization temperature, and a low pH value of Cr(VI) aqueous solution were beneficial for Cr(VI) removal. When pH = 2, the amount of Cr(VI) removal was 99.93 mg/g by the sample obtained from 1 g flax powder impregnated in 4.5 mmol FeSO4/40 mL H2O solution and calcined for 2 hr at 800°C.