Synthetic rutile was prepared by treating Panzhihua titanium slag with H 3 PO 4 followed by leaching. To this end, the effects of oxidation temperature and H 3 PO 4 dosage on the phase transformation of titanium slag were studied by XRD, while the microstructure and composition of the treated slag were characterized by SEM and EDAX. It was determined that roasting with H 3 PO 4 promoted the transformation of titanium slag into rutile. Furthermore, hydrochloric acid leaching of treated titanium slag was investigated in terms of the effect of HCl concentration, and leaching temperature, time and liquid-to-solid mass ratio on leaching. The results show that Fe, Mg, Ca and Al can be effectively removed by leaching with 20wt.% HCl at a liquid-to-solid ratio of 5:1 at 110°C for 2h. It was found that a NaOH leaching step is necessary to remove Si and P to improve the purity of synthetic rutile. Using this process, synthetic rutile containing 95.34% TiO 2 and 0.37% (MgO+CaO) was obtained.