This review article is devoted to our work in the area of MCM-41 type materials modified with iron species. Three types of matrices have been applied: silicate MCM-41, aluminosilicate AlMCM-41, and niobosilicate NbMCM-41. Iron was introduced by various methods: during the synthesis, immobilisation of ferroceneacetic acid (FAA), chemical vapour deposition (CVD), impregnation, cation exchange (IE) and template cation exchange (TIE). Three fundamental features of the prepared materials have been considered: (i) structure, (ii) iron state (coordination, oxidation level, reducibility), and (iii) catalytic activity. The latter was tested in isopropanol decomposition, oxidation of methanol, decomposition of NO, selective reduction of NO with propene, and hydroxylation/polymerisation of phenol. To cite this article: P. Decyk et al., C. R. Chimie 8 (2005).
Cet article de revue présente l’ensemble de nos activités dans le domaine des matériaux de type MCM-41 contenant du fer. Trois types de matrices ont été utilisées : un silicate MCM-41, un aluminosilicate AlMCM-41, et un silicate de niobium NbMCM-41. L’élément Fe a été introduit par diverses méthodes : pendant la synthèse, par immobilisation de l’acide ferrocènacétique (FAA), par dépôt en phase vapeur (CVD), par imprégnation, par échange cationique sur la matrice MCM-41 calcinée (IE) et par échange cationique sur la matrice MCM-41 contenant le structurant organique (TIE). Trois caractéristiques fondamentales des matériaux ainsi préparés ont été considérées : (i) la structure ; (ii) l’état de l’élément fer (coordination, degré d’oxydation, réductibilité) et (iii) l’activité catalytique. Cette dernière caractéristique a été évaluée par des tests catalytiques comme la décomposition de l’isopropanol, l’oxydation du méthanol, la décomposition de NO, la réduction sélective de NO par le propène et l’hydroxylation/polymérisation du phénol. Pour citer cet article : P. Decyk et al., C. R. Chimie 8 (2005).