Zinc oxide derived from processing of the slime obtained in an industrial process of electrolytic zinc obtaining was leached with the aqueous sulfuric acid solution. The effect of temperature and time on the extent of leaching was determined. The conditions lead to zinc recovery of about 90%. It was found that the extent of arsenic leaching did not depend upon the time and temperature of leaching. Next the conditions of the solution purification procedure were determined. It was found that jarosite formation as well as the degree of arsenic removal is connected with trivalent iron concentration in the solution.
Jha, M. K., Kumar, V. & Singh, R. J., (2001). Review of hydrometallurgical recovery of zinc from industrial wastes, Resources Conservation, Recycling, 33, 1-22.
Jarosiński, A, (2007). Exemplary solutions of zinc raw material processing, Waste recycling XI, Kosice, 6-7 December, 177-184.
Malinowski, Cz., Małecki, S. & Jochymek, Ł. (2007), Alternative way of zinc secondary material processing, IX International Conference "Theoretical and practical problems of management of metallurgical and industrial wastes", 16-18 May, 89-95, AGH Faculty of Non-ferrous, 89-95 (in Polish).
Financed by the National Centre for Research and Development under grant No. SP/I/1/77065/10 by the strategic scientific research and experimental development program:
SYNAT - “Interdisciplinary System for Interactive Scientific and Scientific-Technical Information”.